| 断裂伸长率 | 120% | 密度 | 1.14g/cm3 | 弯曲强度 | 58.82MPa |
| 吸水率 | 1.3% | 成型收缩率 | 2.2% | 加工级别 | 注塑级 |
| 特性级别 | 标准级 |
在线订购说明
保障消费者权益，真正做到正品交易，杜绝假冒伪劣产品
021-58958519 13061808058(蒋先生) 13424755533(赵先生)
联系上海松翰
| 021-58958519 | |
| 13061808058(蒋先生) | |
| 13424755533(赵先生) | |
| |
|
|
产品简述
备注
备注:特性：标准粘度
详细数据
订购指南
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | ASTM D-570 | 8.8 | % | |
| 吸水率 | ASTM D-570 | 1.3 | % | ||
| 成型收缩率 | UBEmethod | 2.2 | % | ||
| 成型收缩率 | UBEmethod | 1.7 | % | ||
| 物理性能 | 比重 | ASTM D-792 | 1.14 | ||
| 机械性能 | 弯曲弹性率 | 23° | ASTM D-790 | 11500 | kgf/cm2 |
| 弯曲弹性率 | 23° | ASTM D-790 | 29000 | kgf/cm2 | |
| 弯曲强度 | -30° | ASTM D-790 | 1400 | kgf/cm2 | |
| 1%变形下的压缩强度 | 23° | ASTM D-695 | 210 | kgf/cm2 | |
| 屈服下的伸张强度 | 80° | ASTM D-638 | 400 | kgf/cm2 | |
| 弯曲弹性率 | 80° | ASTM D-790 | 5000 | kgf/cm2 | |
| 屈服下的伸张强度 | 23° | ASTM D-638 | 540 | kgf/cm2 | |
| 弯曲弹性率 | -30° | ASTM D-790 | 42000 | kgf/cm2 | |
| 弯曲强度 | -30° | ASTM D-790 | 1300 | kgf/cm2 | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 120 | ||
| 屈服下的延伸率 | 23° | ASTM D-638 | 6 | % | |
| 断裂下的伸张强度 | 23° | ASTM D-638 | 650 | kgf/cm2 | |
| 挤剪强度 | 23° | ASTM D-732 | 700 | kgf/cm2 | |
| 屈服下的伸张强度 | 80° | ASTM D-638 | 430 | kgf/cm2 | |
| 抗冲击强度 | 23° | ASTM D-256 | 30 | kgf.cm/cm | |
| TABER磨耗率 | ASTM D-1044 | 5 | mg | ||
| 屈服下的伸张强度 | -30° | ASTM D-638 | 1100 | kgf/cm2 | |
| 屈服下的伸张强度 | -30° | ASTM D-638 | 1150 | kgf/cm2 | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 100 | ||
| 1%变形下的压缩强度 | 23° | ASTM D-695 | 110 | kgf/cm2 | |
| 弯曲弹性率 | 80° | ASTM D-790 | 9000 | kgf/cm2 | |
| 弯曲强度 | 23° | ASTM D-790 | 1100 | kgf/cm2 | |
| 挤剪强度 | 23° | ASTM D-732 | 650 | kgf/cm2 | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 65 | ||
| 弯曲强度 | 23° | ASTM D-790 | 600 | kgf/cm2 | |
| 断裂下的延伸率 | 23° | ASTM D-638 | 120 | % | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 90 | ||
| 屈服下的伸张强度 | 23° | ASTM D-638 | 780 | kgf/cm2 | |
| 抗冲击强度 | -30° | ASTM D-256 | 3.0 | kgf.cm/cm | |
| 弯曲弹性率 | -30° | ASTM D-790 | 40000 | kgf/cm2 | |
| 断裂下的延伸率 | 23° | ASTM D-638 | >200 | % | |
| 抗冲击强度 | 23° | 5.0 | |||
| 电气性能 | IEC电路 | UL 746 | 600+ | V | |
| 介电损耗 | 106HZ | ASTM D-150 | 0.08 | ||
| 介电损耗 | 103HZ | ASTM D-150 | 0.02 | ||
| 体积电阻率 | ASTM D-257 | 1015 | Ω.cm | ||
| 介电损耗 | 60HZ | ASTM D-150 | 0.01 | ||
| 抗电弧强度 | ASTM D-495 | 182 | S | ||
| 介电损耗 | 106HZ | ASTM D-150 | 0.02 | ||
| 介电损耗 | 103HZ | ASTM D-150 | 0.07 | ||
| 介电常数 | 106HZ | ASTM D-150 | 4.1 | ||
| 绝缘耐力 | ASTM D-149 | 20 | KV/mm | ||
| 介电损耗 | 60HZ | ASTM D-150 | 0.07 | ||
| 体积电阻率 | ASTM D-257 | 1013 | Ω.cm | ||
| 介电常数 | 60HZ | ASTM D-150 | 3.9 | ||
| 介电常数 | 60HZ | ASTM D-150 | 7.0 | ||
| 介电常数 | 103HZ | ASTM D-150 | 6.0 | ||
| 介电常数 | 103HZ | ASTM D-150 | 3.8 | ||
| 介电常数 | 106HZ | ASTM D-150 | 3.4 | ||
| 热性能 | 热变形温度 | 18.6kgf/cm2 | ASTM D-648 | 90 | °C |
| 燃烧率 | UL 94 | V-2 | |||
| 热变形温度 | 4.6kgf/cm2 | ASTM D-648 | 230 | °C | |
| 熔点 | DSC | 255-265 | °C | ||
| 线性热膨胀系数 | ASTM D-696 | 8 | X的10-5cm/cm/°C | ||