ATI Steel JS700®

牌号ATI Steel JS700®
厂家Allegheny Technologies Incorporated
分类Steel
介绍ATI corrosion resistant engineering alloy, JS700®, is a high-alloy, fully austenitic, superaustenitic stainless steel. This alloy is a proven problem-solver in many applications where corrosive conditions are too severe for standard grades of stainless steel. It has also provided a cost-effective alternative to more expensive nickel-base and titanium-base alloys.

JS700 stainless steel is more highly alloyed than standard stainless steels. It contains nominally 25% nickel, 20% chromium and 4.5% molybdenum. The high molybdenum content is particularly important to the corrosion resistant properties. Molybdenum is used in many stainless steels to improve resistance to both localized and general corrosion. It enhances development of the passive film responsible for the corrosion resistance of stainless, and makes the alloy more noble so that corrosion resistance is improved even under conditions which tend to destroy passivity. The molybdenum content of JS700 steel, at 4.3 to 5.0%, is more than twice the level usually found in the widely-used Type 316 stainless steel.

The chromium content of the JS700 alloy is essential to corrosion resistance. Since chromium contributes to sigma formation, the 20% level was chosen as a satisfactory compromise. The high nickel content not only minimizes sigma, but also contributes markedly to corrosion resistance. The effects of higher nickel are believed to relate more to corrosion propagation than to initiation. As shown in the tabulated corrosion test results, JS700 steel far outperforms Type 317LM, a steel with similar molybdenum content and only slightly lower chromium, but much lower nickel.

The combination of the three major alloying elements gives JS700 stainless steel a high degree of resistance to stress corrosion cracking. No field service failures from stress corrosion cracking in JS700 alloy have been reported to date.

JS700 steel has a relatively low carbon content, plus columbium stabilization to tie up the remaining carbon. This stabilization guards against intergranular corrosion due to carbide precipitation (sensitization) in areas such as weld heat affected zones even more effectively than with a 0.020% carbon level without stabilization. JS700 alloy will, in fact, pass a demanding Huey test in the furnace sensitized condition.
在线客服:  点击这里给我发消息 点击这里给我发消息 上海松翰塑胶
申请技术报告方式

可通过以下我公司客服QQ,索要技术报告

客服1:点击这里给我发消息 客服2:点击这里给我发消息
Allegheny Technologies Incorporated 产品展示 种类
ATI Steel ATI 418 SPL™ Steel
ATI Steel ATI 904L™ Steel
ATI Steel ATI 332™ Steel
ATI Steel Zeron® 100 Steel
ATI Steel Grain-Oriented Electrical Steel (Grade M-4) Steel
ATI Steel ATI 17-7™ Steel
ATI Steel ATI 219™ Steel
ATI Steel ATI 305™ Steel
ATI Steel ATI 800H™ Steel
ATI Steel JS700® Steel

订购说明

上海松翰塑化科技有限公司订货流程

【订购导引】
       我司所销售所有产品均为原厂原包,均可提供相关资料报告(如:物性表,MSDS报告,UL报告,COA报告,SGS报告,FDA等)!
       如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告,请您通过电话或是客服QQ与我联系!

【物流说明】
       自接到贵司订购单24小时内发货,珠三角,长三角,北京,天津均支持代收货款。货物送达后,请第一时间检查外包装,如发现物流过程中出现大量包装损坏及原料外漏的,请让物流人员出具证明并保存,并在24小时内与我司客服部取得联系。


【订购流程】
订货流程



【退换货处理】
退货:
依照中华人民共和国消费者保护法规,在您收到货品7天内,若发现您收到的商品有瑕疵或损坏,您可以要求退货,请主动与本公
司联络,敝公司接到您的商品之后,会将您的购物金额全额退回。

换货:
若您收到的商品有瑕疵或损坏,请您于7天内与本公司联络,本公司有专人处理换货事宜。
版权所有 © Shshsj.com All Rights Reserved