Outokumpu 1.4372

牌号Outokumpu 1.4372
厂家Outokumpu
分类Steel
介绍Austenitic chromium-manganese stainless steel
Type 17Cr-5Ni-7Mn stainless steel: EN 1.4372, AISI 201
  • A low nickel variation to standard austenitic stainless steel grade 1.4301.

Applications
  • Applications like cookware, washing machine baskets and hose clamps are generally used. In contact with food there are national regulations and in some of them chromium content Min. 17 % and nickel content Min. 4 % are required for cutlery materials.
  • Due to its high strength, corrosion resistance and competitive costs, steel grade is suited for the transportation industry.
  • Material is used also in architectural applications, like elevators, windows, doors and lamp posts.

Welding
  • Conventional welding methods and filler materials applied to 300-series can be used. Proper shield against possible Mn-oxide fumes is recommended.
  • Sensitive to intergranular corrosion in the weld heat affected zone when material thickness exceeds 6 mm.
  • Cleaning of the weld seam is important for corrosion resistance. Pickling is recommended.

Fabrication
  • Formability is good, but the forces needed and the elastic return are bigger compared to carbon steels and grade 1.4301 / AISI 304.
  • Steel grade 1.4372 suits for demanding forming operations as well as bending, and drawing due to its high elongation to fracture.
  • Work hardening is pronounced. Sensitivity to delayed cracking after demanding forming processes may be observed, e.g. when deep drawing ratio is close to 2,0 and residual tensile stresses are present.
  • Typically Mn-alloyed grades have a slightly lower surface reflectivity compared to the CrNi-grade 1.4301. This can lead for the need of increased material removal in further polishing and brushing processes.

Corrosion resistance
  • Outokumpu produces grade 1.4372 typically with a chromium content of about 17 wt-% and a nitrogen content of 0,20 wt-% giving the material a corrosion resistance close to grade 1.4301 / AISI 304. Repassivation enhanced by nickel is lower than that of grade 1.4301.
  • In chloride containing solutions pitting and crevice corrosion is possible depending on various parameters like chloride concentration, temperature, pH value, redox potential, crevice geometry and others.
  • Oxidation resistance is good and comparable to steel grade 1.4310 / AISI 301 up to 840°C.
  • The best material performance is reached usually with the help of adequate design, correct post-weld treatment and regular cleaning during use (if applicable).
在线客服:  点击这里给我发消息 点击这里给我发消息 上海松翰塑胶
申请技术报告方式

可通过以下我公司客服QQ,索要技术报告

客服1:点击这里给我发消息 客服2:点击这里给我发消息
Outokumpu 产品展示 种类
Outokumpu 4841 Steel
Outokumpu 2304 Steel
Outokumpu 4878 Steel
Outokumpu 1.4509 Steel
Outokumpu 4501 Steel
Outokumpu 4435 Steel
Outokumpu 153 MA™ Steel
Outokumpu 4318 Steel
Outokumpu LDX 2101® Steel
Outokumpu LDX 2404™ Steel

订购说明

上海松翰塑化科技有限公司订货流程

【订购导引】
       我司所销售所有产品均为原厂原包,均可提供相关资料报告(如:物性表,MSDS报告,UL报告,COA报告,SGS报告,FDA等)!
       如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告,请您通过电话或是客服QQ与我联系!

【物流说明】
       自接到贵司订购单24小时内发货,珠三角,长三角,北京,天津均支持代收货款。货物送达后,请第一时间检查外包装,如发现物流过程中出现大量包装损坏及原料外漏的,请让物流人员出具证明并保存,并在24小时内与我司客服部取得联系。


【订购流程】
订货流程



【退换货处理】
退货:
依照中华人民共和国消费者保护法规,在您收到货品7天内,若发现您收到的商品有瑕疵或损坏,您可以要求退货,请主动与本公
司联络,敝公司接到您的商品之后,会将您的购物金额全额退回。

换货:
若您收到的商品有瑕疵或损坏,请您于7天内与本公司联络,本公司有专人处理换货事宜。
版权所有 © Shshsj.com All Rights Reserved